Electrolysis E Coating Car Body Painting With Better Substrate Hiding

Brand Name : HAOLISEN

Model Number : HS-6060LB/HS-2668G

Certification : IATF16949 , ISO9001

Place of Origin : Shanghai China (Mainland)

MOQ : Negotiation

Price : Negotiation

Supply Ability : 200 Tons Per Day

Delivery Time : 30-60 Days

Packaging Details : 50kg、60 kg、200kg、1000kg packaging barrels

main ingredients : carbon black, kaolin

Application field : car covers

Performance : film smooth

Cooperation case : ANHUI Xin hong traffic,

Contact Now

Solution for the car covers electrophoresis paint.

Product Introduction

HS-6060LB/HS-2668G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.

This product features shown below: 

Coating fullness of good, better substrate hiding .
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
The appearance of the coating is flat, delicate, smooth.
Good stability of bath can adaptable for a longer updating cycle. 
Excellent leveling coating,good bonding force and compatibility with plastic powder.

Filling tank proportion and method

⑴ Bath preparation

Ratio:

Resin 1000.00-1250.00

Paste 250.00

DI water 1500.00


Total 2750.00

⑵ Ripening conditions

Sample quantity 3000~4000g
Container 4L (Diameter 16cm)
Tank temperature 28-30 ℃
Time 24~48Hr
Mixed conditions impeller diameter 8cm (speed 200rpm)


(3) Coating conditions

Experimental panel phosphated cold-rolled steel plate
Tank temperature 28-35℃
Pole ratio A/C = 1/2 ~ 1/4
Distance of electrodes 15cm
ED time For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions (175-185)℃×(20-30)min (Keeping temperature of parts coated)


Product film performance

Project Indicator Test standard
Appearance Normal / abnormal Normal Ocular estimate
Hardness 2H GB/T 6739
Cup drawing mm ,≥ 6 GB/T 9753
Adhesion Level 0 GB/T 9286
Flexibility mm 1 GB/T 1731
Impact kg·cm 50 GB/T 1732
Gloss 60 50-80 GB/T 9754
Water resistance h,(23±2)℃,≥ 240 GB/T 1733
Acid resistance h,(50g/L H2SO4),≥ 72 GB/T 9274
Alkali resistance h,(50g/L NaOH),≥ 48 GB/T 9274
*Salt spray resistanc​e h,(film thickness ≥ 20μm) ,≥ 1000 GB/T 1771

* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.

Customer production site

Electrolysis E Coating Car Body Painting With Better Substrate Hiding


Product Tags:

cathodic electrocoating

      

car paint coating

      
Wholesale Electrolysis E Coating Car Body Painting With Better Substrate Hiding from china suppliers

Electrolysis E Coating Car Body Painting With Better Substrate Hiding Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: HLS Coatings (Shanghai)Co.Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)
 
Inquiry Cart 0