Special Air vents white electrophoresis paint
Product Introduction :
|
AED-2000LB/AED-2000 White anodic electrophoretic coatings for auto is the 1th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd..
This coating has excellent weather resistance, smooth appearance.
|
|
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin. The coating that does not contain tin element meet the latest environ-mental regulations of European Union, North America, Japan and other requirements in advance, which is the inevitable trend of future environ-mental coating and low cost; meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal,
such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.
|
This product features shown below:
Have excellent weather resistance
Excellent yellowing resistance
Main ingredients:
Matrix resin: Acrylic modified epoxy resin
Curing agent: Fully enclosed multi isocyanate
Additives: surface active agent, prevent shrinkage cavity agent
Ngan: titanium dioxide, kaolin
Product quality data:
| Project |
Technical data |
Test standard |
Resin
(AED-2000LB) |
White Paste (AED-2000) |
| pH |
25℃ |
8.5±0.5 |
—— |
GB/T 9724 |
| Conductivity |
25℃, μs/cm |
800±500 |
—— |
HG/T 3334 |
| Appearance |
—— |
Milky white liquid |
White viscous liquid,no agglomeration |
Visual |
| Storage stability |
No stratified state, and there were no obvious difference compared to before storage |
In 5-35 ℃ temperature 1 year |
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Product film performance:
| Project |
Indicator |
Test standard |
| Appearance |
Normal / abnormal |
Normal |
Ocular estimate |
| Hardness |
≥ |
3H |
GB/T 6739 |
| Cup drawing |
mm ,≥ |
6 |
GB/T 9753 |
| Adhesion |
Level |
1 |
GB/T 9286 |
| Flexibility |
mm |
1 |
GB/T 1731 |
| Impact |
kg·cm |
50 |
GB/T 1732 |
| Gloss |
60 |
5-10 |
GB/T 9754 |
| Acid resistance |
h,(50g/L H2SO4),≥ |
20 |
GB/T 9274 |
| Alkali resistance |
h,(50g/L NaOH),≥ |
24 |
GB/T 9274 |
| *Salt spray resistance |
h,(film thickness ≥ 20μm) ,≥ |
600 |
GB/T 14522 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.